B-Stage Epoxy Mold Compound Systems

B-Stage Epoxy Molding Compound Cross-Linking

By definition, once a resin and hardener are mixed, the system becomes a B-stage epoxy system. This definition however, is too vague for our purposes. What we need is a better explanation of this effect, and what it means in terms of handling a B-Stage epoxy system such as epoxy mold compounds.

Simply put, a B-stage epoxy system is one wherein the cross-linking reaction (ie. the curing, or hardening phase) is initiated, but is not yet complete. The rate of this reaction is dependent on two factors: time and temperature. At higher temperatures (ie epoxy molding conditions), this hardening reaction occurs very quickly. At lower conditions, this reaction occurs more slowly. The general rule of thumb for epoxy mold compounds is that every 10°C either doubles or halves the rate of reaction.

The problem with this general rule is that it is oversimplified. Yes, the rate of reaction is affected significantly by exposure to higher temperatures. However, at lower temperatures – especially at typical epoxy storage temperatures of 5-8°C, this reaction occurs at such a slow rate that it is barely measurable.

Furthermore, for epoxy mold compounds formulated with catalysts – these lower storage temperatures are far below the minimum activation temperature (sometimes called the “kick-off” temperature) is never reached. This activation temperature is essential for achieving full cure, and without it, the complete reaction or cross-linking never fully takes place.

It is important to understand therefore, which properties are affected during this B-stage staging process, to which extent these properties are affected, and what effect these changes have on final material properties.

As it concerns one-part epoxies and epoxy mold compounds, exposure to higher than recommended storage temperatures over time affects two specific material properties: minimum achievable viscosity and spiral flow.

Please stay tuned for the next part in this series to explore the behaviour of epoxy molding compounds.

Please visit us at www.caplinq.com to learn more about our whole range of epoxy molding compounds including our semiconductor-grade epoxy mold compounds, industrial-grade epoxy molding compounds, and ouroptically clear epoxy molding compounds (CMC). If you have any other questions about B-stage or the effects of time and temperature on the epoxy mold compounds please feel free to leave a comment below or don’t hesitate to contact us.

About Chris Perabo

Chris is an energetic and enthusiastic engineer and entrepreneur. He is always interested in taking highly technical subjects and distilling these to their essence so that even the layman can understand. He loves to get into the technical details of an issue and then understand how it can be useful for specific customers and applications. Chris is currently the Director of Business Development at CAPLINQ.

1 thoughts on “B-Stage Epoxy Molding Compound Cross-Linking

Leave a Reply

Your email address will not be published. Required fields are marked *